Glass textile sleeving with silicone elastomer coating produced with the process of thermal treatment and vulcanization is the non-alkali fiberglass braided sleeving coated with silicone rubber. This sleesivng possesses good qualities of dielectric, high temperature resistance. It can be used for wiring insulation and mechanical protection for electrical machinery and electrical appliances.
Specifications︰
| Bore Diameter | Wall Thickness | ||
| Nominal (mm) | Tolerance （±） | Minimum | Maximum |
| 0.5,0.8 | ±0.10 | 0.20 | 0.50 |
| 1.0,1.5 | ±0.20 | 0.20 | 0.60 |
| 2.0,2.5,3.0 | ±0.20 | 0.20 | 0.70 |
| 3.5,4.0,5.0,6.0 | ±0.25 | 0.30 | 0.70 |
| 7.0,8.0 | ±0.25 | 0.30 | 1.00 |
| 9.0,10.0 | ±0.50 | 0.40 | 1.00 |
| 12.0 | ±0.50 | 0.40 | 1.20 |
| 14.0,16.0,18.0,20.0,23.0 | ±1.00 | 0.40 | 1.20 |
| 25.0,27.0,30.0 | ±1.00 | 0.40 | 1.40 |
Advantages︰
| Performance | Requirements | ||
| Breakdo wn Voltage（KV） | Median | Median | Minimum value |
| under normal（23±2℃） | ≥4.0 | ≥2.5 | |
| High temperature（155±2℃） | ≥2.0 | ≥1.5 | |
| Moist heat treatment | ≥1.5 | ≥1.2 | |
| Resistance to soldering heat | To maintain the temperature of the solder at 260 ° C ± 5 ° C, the middle of the hose vertical section of the lower end of 6mm immersed in the molten solder bath, tinned copper maintained in the molten solder bath 15s ± 1s. Hose shall not crack or obvious swelling. | ||
| Bending resistance after heating | Temperature: 180 ° C ± 3 ° C, processing time 48h ± 1h, hose wrapped around the mandrel, the film should not be disengaged or cracking the glass tube. | ||
| Bending low temperatures | Temperature: ≤ -35 ℃± 2 ° C, the processing time of 240min ± 10min, the outside of the paint film should glass tube disengaged or cracking. | ||
| Spread of flame resistance | ≤60S | ||
| Temperature index | 200℃ | ||